Compatibility of materials for macroencapsulation of inorganic phase change materials: experimental corrosion study
Data de publicació2016
Farid, Mohammed M.
MetadadesMostra el registre d'unitat complet
The potential of the use of salt hydrates MgCl2·6H2O (bischofite) with typical impurities of the Salar de Atacama as a thermal energy storage material was evaluated with special attention to its corrosion behavior. Bischofite behavior is compared with that of commercial salt MgCl2·6H2O. The corrosion tests were conducted with metal sheets (copper, aluminum and stainless steel) partially immersed in molten salt hydrates at a temperature of 120 °C during 1500 h. The results showed minimum corrosion on all the immersed surfaces of all the metals. However, very sever corrosion was observed at the salt/air interface due to a known phenomenon of oxygen enhanced corrosion usually found even with water at ambient temperature. The corrosion products were determined with scanning electron microscopy (SEM-EDX) and X-ray diffraction (XRD) technique. For salts hydrates bischofite and MgCl2·6H2O, the results show the formation of cuprite (Cu2O) and hematite (Fe2O3) on copper and stainless steel samples, respectively. For all cases studied in the present work, several chloride compounds were identified as corrosion products.
És part deApplied Thermal Engineering, 2016, vol. 107, p. 410-419
Projectes de recerca europeus
Mostrant elements relacionats per títol, autor i matèria.
Galazutdinova, Yana; Grágeda, Mario; Cabeza, Luisa F.; Ushak, Svetlana (Wiley, 2017)In this study, an inorganic mixture based on bischofite (industrial by‐product) was developed and characterized for its application as a phase change material for low‐temperature thermal energy storage. The most appropriate ...
Energy savings due to the use of PCM for relocatable lightweight buildings passive heating and cooling in different weather conditions Marin, Paula; Saffari Tabalvandani, Mohammad; Gracia Cuesta, Alvaro de; Zhu, Xibingyan; Farid, Mohammed M.; Cabeza, Luisa F.; Ushak, Svetlana (Elsevier, 2016)Relocatable, transportable or off-site constructed lightweight buildings typically undergo sharp indoor temperature fluctuations in the heating and cooling seasons due to the lack of sufficient thermal mass in their ...
Preparation and characterization of an inorganic magnesium chloride/nitrate/graphite composite for low temperature energy storage Galazutdinova, Yana; Vega, Mariela; Grágeda, Mario; Cabeza, Luisa F.; Ushak, Svetlana (Elsevier, 2018)In this study, an inorganic mixture of 40 wt% MgCl2·6H2O and 60 wt% Mg(NO3)2·6H2O was impregnated into two types of the expanded graphite (EG): EG flakes and EG matrix. Different methods of preparation usually used in the ...