Thermophysical characterization of a by-product from the non-metallic industry as inorganic PCM
Data de publicació2015
MetadadesMostra el registre d'unitat complet
Physical characterization and thermal properties of bischofite, a by-product from the non-metallic industry, were determined and compared with those to MgCl2 6H2O with the idea of using it as phase change material in thermal energy storage applications. The melting point and heat of fusion were measured
in the temperature range from 30 1C to 150 1C, where Tfus and ΔHfus were 100 1C and 115 kJ/kg for bischofite, and 114.5 1C and 135 kJ/kg for MgCl2 6H2O. The solid heat capacity was determined from 25 1C to 60 1C, being 2.1 kJ/(kg K) at 60 1C for both samples. The measurements of the liquid heat capacity of bischofite were done from 115 1C to 125 1C and the Cp showed linear increase from 1.71 kJ/(kg K) to 3.01 kJ/(kg K). The thermal stability test (30 heating/cooling cycles) of bischofite and MgCl2 6H2O shows subcooling of about 37 K and 29 K, respectively. The solid and liquid densities were determined using the pycnometrically method; for bischofite, ρsolid decrease from 1686 (at 30 1C) to 1513 kg/m3 (at 50 1C) and ρliq was 1481 kg/m3 (at 115 1C). Based on the thermophysical properties evaluated, the energy storage density was evaluated for both materials, being 170 J/cm3 for bischofite and 192 J/cm3 for MgCl2 6H2O. This study established that bishofite is a promissory PCM with similar thermophysical characteristics to magnesium chloride hydrate, but with a lower cost. Nevertheless, further work is needed to overcome the two main problems found, subcooling and segregation of the material.
És part deSolar Energy Materials and Solar Cells, 2015, vol. 132, p. 385-391
Mostrant elements relacionats per títol, autor i matèria.
Use of polyethylene glycol for the improvement of the cycling stability of bischofite as thermal energy storage material Gutiérrez, Andrea; Ushak, Svetlana; Galleguillos, Hector; Fernández, Ángel G.; Cabeza, Luisa F.; Grágeda, Mario (Elsevier, 2015)Bischofite is a by-product of the non-metallic mining industry. It has been evaluated as phase change material in thermal energy storage, but it shows little cycling stability, therefore in this paper the mixture of ...
Gasia, Jaume; Gutiérrez, Andrea; Peiró Bell-lloch, Gerard; Miró, Laia; Grágeda, Mario; Ushak, Svetlana; Cabeza, Luisa F. (Elsevier, 2015)The selection of the proper thermal energy storage (TES) material for an application is crucial. On the one hand, these materials should have suitable thermal properties for the operational temperatures range of the ...
Ushak, Svetlana; Gutiérrez, Andrea; Galazutdinova, Yana; Barreneche Güerisoli, Camila; Cabeza, Luisa F.; Grágeda, Mario (John Wiley & Sons, 2016)Brines coming from salted lakes such as that at the Atacama desert in Chile produce by-products or wastes which today are stored in the nearby from the production areas. Bischofite is one of those by-products, and therefore, ...