Experimental characterization of a solid industrial by-product as material for high temperature sensible thermal energy storage (TES)
Data de publicació2014
Navarro, Maria E.
Fernández Renna, Ana Inés
MetadadesMostra el registre d'unitat complet
Nowadays, industrial processes use large quantities of fuel and electricity that produce heat, but much of which is wasted either to the atmosphere or to water. Many types of equipment have been developed to re-use some of this waste heat. Waste heat usefulness is determined by its temperature and
its exergy; the higher the temperature the higher the quality or value. There are mainly three reversible methods to store it: sensible, latent and chemical. In this case, a solid by-product from the potash industry is tested in two different shapes to be used for industrial sensible heat recovery in high temperature, in a range of 100–200 ºC. This heat recovery could be used for cogeneration, energy efficiency measures, passive heat recovery, solar cooling, etc. Within all the properties that define the suitability of a material to store sensible heat, waste materials stand out especially for their low costs and availability. This heat recovery could be used for cogeneration, energy efficiency measures, passive heat recovery, solar cooling, etc. For that, a complete analysis of thermophysical properties was done both, at laboratory and a pilot plant scale. At the laboratory, the material composition was found to be NaCl as major phase. With differential scanning calorimetry (DSC) the specific heat capacity was determined as 0.738 kJ/kgºC. The thermal stability was checked from ambient temperature to 800 ºC and the density and the conductivity at room temperature were also calculated. Also, a corrosion test was performed using samples of stainless steel at three degradation times, these results were compared with those obtained with Solar salt, a commercial and extended option for thermal energy storage (TES) applications at high temperature. At pilot plant scale, using 59 kg of storage material, thermal cycles were performed with the storage material heating and cooling it from 100 to 200 ºC varying parameters as the heat transfer fluid (HTF) flow rate and the duration of the cycles.
És part deApplied Energy, 2014, vol. 113, p. 1261–1268
Mostrant elements relacionats per títol, autor i matèria.
Navarro, Maria E.; Martínez, Mònica; Gil, Antoni; Fernández Renna, Ana Inés; Cabeza, Luisa F.; Olives, R.; Py, Xavier (Elsevier, 2012)Alternative low cost materials are evaluated through the valorization of by-products derived from mining and metallurgical industry for solid sensible heat based energy storage systems. They were used either as received ...
Ushak, Svetlana; Gutiérrez, Andrea; Galleguillos, Hector; Fernández, Ángel G.; Cabeza, Luisa F.; Grágeda, Mario (Elsevier, 2015)Physical characterization and thermal properties of bischofite, a by-product from the non-metallic industry, were determined and compared with those to MgCl2 6H2O with the idea of using it as phase change material in ...
Advances in the valorization of waste and by-product materials as thermal energy storage (TES) materials Gutiérrez, Andrea; Miró, Laia; Gil, Antoni; Rodríguez Aseguinolaza, Javier; Barreneche Güerisoli, Camila; Calvet, Nicolas; Py, Xavier; Fernández Renna, Ana Inés; Grágeda, Mario; Ushak, Svetlana; Cabeza, Luisa F. (Elsevier, 2016)Today, one of the biggest challenges our society must face is the satisfactory supply, dispatchability and management of the energy. Thermal Energy Storage (TES) has been identified as a breakthrough concept in industrial ...